Polymaker PC-ABS
This Specialty family provides unique filaments from Polymaker to unlock new 3D printing applications.
Polymaker PC-ABS is a PC/ABS polymer blend which offers excellent toughness and heat resistance while displaying good surface finish and good compatibility with metal plating.
PolyLite PLA features Jam-Free technology: Jam-Free™ technology improves the heat stability of Polymaker’s PLA filaments with softening temperatures over 140 °C. As a result, Polymaker’s PLA filaments show minimal softening in the “cold end” and can melt rapidly once entering the heating zone, leading to excellent printing quality with zero risk of nozzle jams.
When printing with Polymaker PC-ABS it is recommended to use a heated chamber.
It is recommended to anneal the printed part right after the printing process to release the residual internal stress when not using a heated chamber.
Annealing settings: 90˚C for 2h
- Diameter1.75 mm, 2.85 mm
- Material TypePC/ABS
- ColorBlack, White
- Net Weight1 kg
- BrandPolymaker
- Nozzle Temperature250˚C – 270˚C
- Glass Transition Temperature109˚C
- Charpy Impact Strength25.8 ± 1.4 (kJ/m2)
- Bending Strength66.3 ± 1.3 (MPa)
- Tensile Strength39.9 ± 1.0 (MPa)
- Young’s Modulus1832 ± 65 (MPa)
- Drying Settings80˚C for 8h
- Cooling FanOFF
- Bed SurfaceAlmost any surface with a thin coat of Magigoo PC
- Bed Temperature30 – 50mm/s
- Printing Speed30 – 50mm/s
- Vicat Softening Temperature109˚C
- Recommended Support MaterialsPolyDissolve S2
- Chamber Temperature90˚C – 100˚C