PolyMide PA6-CF
PolyMide is a family of Nylon/polyamide based filaments. Produced with Polymaker’s Warp-Free technology, PolyMide filaments deliver engineering properties intrinsic to Nylon and ease of printing.
PolyMide PA6-CF is a carbon fiber reinforced PA6 (Nylon 6) filament. The carbon fiber reinforcement provides significantly improved stiffness, strength and heat resistance with outstanding layer adhesion.
PolyMide PA6 CF features Polymaker's Warp-Free technology and Fiber Adhesion™ technology: Warp-Free technology enables the production of Nylon-based filaments that can be 3D printed with excellent dimensional stability and near-zero warpage. This is achieved by the fine control of microstructure and crystallization behavior of Nylon, which enables the material to fully release the internal stress before solidification.Fiber Adhesion technology improves the layer adhesion of fiber reinforced materials, by optimizing the surface chemistry of the fibers to achieve better dispersion and bonding to the matrix. This results in better strength along the Z-axis and reduced mechanical anisotropy.
Technical Data Sheet - Download
SafetyData Sheet - Download
- Diameter1.75 mm, 2.85 mm
- Material TypeNylon
- ColorBlack
- Net Weight2 kg, 500 g
- BrandPolymaker
- Nozzle Temperature280˚C – 300˚C
- Vicat Softening Temperature180˚C
- Printing Speed60mm/s
- Bed Temperature25˚C – 50˚C (Do NOT exceed 50 ˚C)
- Bed SurfaceAlmost any surface with a thin coat of PVA glue or Magigoo PA
- Cooling FanOFF
- Drying Settings80˚C for 12h
- Young’s Modulus7453 ± 656 (MPa)
- Tensile Strength105.0 ± 5.0 (MPa)
- Bending Strength169.0 ± 4.7 (MPa)
- Charpy Impact Strength13.34 ± 0.52 (kJ/m2)
- Glass Transition Temperature67˚C
- Melting Temperature220 (°C)
- Heat Deflection Temperature (ISO 75 1.8 MPa)196 ˚C
- Heat Deflection Temperature (ISO 75 0.45 MPa)215 ˚C
- Recommended Support MaterialsPolyDissolve S1
- Features
- High StrengthYes
- Carbon FiberYes